We are Manufacturer, Supplier, Exporter, Services Provider of Epoxy Anticorrosive Primers, Polyurethane Top Coats, Polyurethane Finish Paints, Two Pack Epoxy Top Coats, Two Pack Epoxy Coal Tar Blacks, Chlorinated Rubber Paints, Synthetic Q.D. Enamels, Stoving Paints and our setup is situated in Pune, Maharashtra, India. We provide these products in different applications like Industrial Machine Sectors, Engines & Pumps. These products have excellent chemical resistance, oil / Lubricant resistance.

POLYURETHANE FINISH PAINT

TWO PACK EPOXY TOP COAT

Product Description :   EPOXY TOP COAT
Recommended use : Transformers , Radiators , Machine Tools, MS Tanks
Features : • Excellent Chemical Resistance 
• Smooth & glossy finish.
• Excellent adhesion
Physical Properties :
Colour Shade As per customer requirement
Volume Solids 50 (± 5%)
D.F.T. 30 to 40 microns
Theoretical spreading rate 8 to 9 sq. meter @ D.F.T. 25-30 μ
Flash point Base - 26°C; Hardner - 28°C
Sp. Gravity Base 1.20 (±0.1 ) kg per Ltr.

Hardner 0.90 (± 0.05) kg / Ltr

 

Surface Preparation : • Surface to be coated should be completely clean , dry and free from contamination.
• Remove oil & grease with suitable solvent or detergent
• Remove rust, mill scale and other loose material by wire mesh / abrasive blasting
Application :
Application Conditions Ambient temperature shall be above 10°C and relative humidity shall be below 85%. Adequate ventilation shall be provided in confined spaces
Mixing Stir each component with mechanical stirrer before mixing
Mixing ratio Paint : 2 parts, Hardner : 1 part , Thinner : 1 parts (by volume)
Application method By air assisted spray gun
Pot Life Minimum 4 hours at 30°C
(Pot life may be reduced at higher temperature)
Drying Time Surface Dry – 20 to 30 minutes
Touch Dry – 3 to 4 hours
Over Coating Minimum 8 hours
Typical undercoat Epoxy Primer
Shelf Life Base : 12 months; Hardner : 12 months from the date of mfg.

TWO PACK EPOXY COAL TAR BLACK

Product Description :   EPOXY Anticorrosive Primer 
Recommended use : Steel Structures, traction batteries, Chemical plants , MS Tanks
Features : • Excellent Chemical Resistance 
• High Performance Corrosion control
• Quick Drying
• Can be applied on wet surface
Physical Properties :
Colour Shade Black
Volume Solids 55 (± 5 %)
D.F.T. 30 to 40 microns
Theoretical spreading rate 9 to 10 sq. meter @ D.F.T. 25 μ
Flash point Base - 26°C ; Hardner - 28°C
Sp. Gravity Base 1.25 (± 0.1 ) kg per Ltr.
Hardner 0.85 (± 0.05) kg / Ltr
Surface Preparation : • Surface to be coated should be completely clean , dry and free from contamination.
• Remove oil & grease with suitable solvent or detergent
• Remove rust, mill scale and other loose material by wire mesh / abrasive blasting
Performance Properties :

Acid / Alkali Resistance-  for 10% solution – 24 hours
Salt Spray – passes 300 hours

Application :
Application Conditions Ambient temperature shall be above 10°C and relative   
humidity shall be below 85%. Adequate ventilation shall be  
provided in confined spaces
Mixing Stir each component with mechanical stirrer before mixing
Mixing ratio Paint : 4 parts, Hardner : 1 part , Thinner : 1.5 parts (by volume)
Application method By air assisted spray gun/ airless spray gun
Pot Life Minimum 6 hours at 30°C
(Pot life may be reduced at higher temperature)
Drying Time Surface Dry – 20 to 30 minutes
Touch Dry – 4 to 5 hours
Typical undercoat Epoxy Primer
Shelf Life Base : 12 months; Hardner : 12 months from the date of mfg.

CHLORINATED RUBBER PAINT

Product Description :   Protective and chemical resistance paint
Recommended use : Steel Structures, traction batteries, Chemical plants , MS Tanks
Features : • Excellent Chemical Resistance & Acid –Alkali resistance 
• Water resistance
• Quick Drying
Physical Properties :
Colour Shade All Pigmented shades (except white)
Volume Solids 40 (± 5%)
D.F.T. 25 to 30 microns
Theoretical spreading rate 5 to 6 sq. meter @ D.F.T. 25 μ
Flash point 23°C
Sp. Gravity Base 1.10 (± 0.1 ) kg per Ltr.
Surface Preparation : • Surface to be coated should be completely clean , dry and free from contamination.
• Remove oil & grease with suitable solvent or detergent
• Remove rust, mill scale and other loose material by wire mesh / abrasive blasting
Performance Properties :

Acid / Alkali Resistance-  for 10% solution – 24 hours
Salt Spray – passes 300 hours for total system

Application :
Application Conditions Ambient temperature shall be above 10°C and relative humidity shall be below 85%. Adequate ventilation shall be provided in confined spaces
Mixing Stir well with mechanical stirrer before mixing
Mixing ratio Paint : 2 parts, Thinner : 1 part (by volume)
Application method By air assisted spray gun
Drying Time Surface Dry - 10 to 15 minutes
Touch Dry – 15 to 20 minutes
Typical undercoat Epoxy Primer
Shelf Life Base : 12 months from the date of mfg.

SYNTHETIC Q.D. ENAMELS

Product Description :   Quick Drying Enamel Paints
Recommended use :

Steel Structures, Auto body –Commercial Vehicles & Auto parts

Features : • Excellent drying properties 
• Smooth & Glossy Finish
• Good Durability
Physical Properties :
Colour Shade As per customer’s requirement
Volume Solids 52 (± 3%)
D.F.T. 25 to 30 microns
Theoretical spreading rate 8 to 9 sq. meter @ D.F.T. 25 μ
Flash point 26° C
Sp. Gravity Base 1.10 (± 0.1 ) kg per Ltr.
Surface Preparation : • Surface to be coated should be completely clean, dry and free from contamination.
• Remove oil & grease with suitable solvent or detergent
• Remove rust, mill scale and other loose material by wire mesh / abrasive blasting
Performance Properties :

Weathering- 100 hrs. (10% gloss reduction accepted)
Salt Spray – passes 140 hours for total system

Application :
Application Conditions Ambient temperature shall be above 10°C and relative
humidity shall be below 85%. Adequate ventilation shall be
provided in confined spaces
Mixing Stir well with mechanical stirrer before application
Mixing ratio Paint : 4 parts, Thinner : 1 part (by volume)
Application method

By air assisted spray gun

Drying Time

Surface Dry – 25 to 30 minutes
Touch Dry – 4 to 5 hours

Typical undercoat Q.D. Primer
Shelf Life 12 months from the date of mfg.

STOVING PAINT

Product Description :   Stoving Enamel Paint
Recommended use :

Auto body - Commercial Vehicles , Two wheelers, Auto components & steel Furniture 

Features : • Excellent Hardness
• Smooth & Glossy Finish
• Good Durability
Physical Properties :
Colour Shade As per customer’s requirement
Volume Solids 42 (± 3%)
D.F.T. 30 to 35 microns
Theoretical spreading rate 5 to 6 sq. meter @ D.F.T. 25 μ
Flash point 23°C
Sp. Gravity Base 1.10 (± 0.1 ) kg per Ltr.
Surface Preparation : • Surface to be coated should be completely clean , dry and free from contamination.
• Remove oil & grease with suitable solvent or detergent
• Remove rust, mill scale and other loose material by wire mesh / abrasive blasting
Performance Properties : Weathering – 400 hrs. (10% gloss reduction accepted)
Salt Spray – passes 180 hours for total system
Petrol – Diesel resistance - Passes
Application :
Application Conditions Ambient temperature shall be above 10°C and relative   
humidity shall be below 85%. Adequate ventilation shall be  
provided in confined spaces
Mixing Stir well with mechanical stirrer before application
Mixing ratio Paint : 3 parts, Thinner : 1 part (by volume)
Application method By air assisted spray gun
Stoving schedule 120° C (± 5°C) for 30 minutes
Typical undercoat Stoving  Primer
Shelf Life 12 months from the date of mfg.

Two Pack Epoxy High Build Mastic Coating :

This Epoxy mastic coating is specially developed for application for untreated or unprepared surface. It can be apply on wet surface. It has excellent adhesion & Chemical resistance.

APPLICATION : This coating can be used as universal primer for steel structure, pipelines, tanks, Chemical plants. This primer can be over coated with Epoxy, P.U. or quick drying paints.

  • Excellent adhesion
  • Excellent Chemical Resistance
  • Longer Pot Life
  • Can achieve High D.F.T
  • 500-700 hours salt spray