Commercial Vehicle Sectors

‘PIONEER COATS’ is a leading Paint manufacturer, who can supply quality paints to leading Bus Body builders in India.

Read More

Auto Component

We have exact and perfect coating solutions for all auto components .

Read More

Industrial Machine Sectors, Engines & Pumps

We can supply primers and paints for CNC Machines, Engines & Pumps

Read More

Power & Electric Sectors

We can supply primers and paints for Power & Electric Sectors

Read More

Steel Pre Structures

We can supply primers and paints for Steel Pre Structures & Grating

Read More

Wood Coatings

We can supply Wood Coatings, PUD Coatings for Wood

Read More

Pipes & Tubes

We can supply paints for industrial Pipes & Tubes

Read More

Vehicle Sectors Auto Component Industrial Machines Power & Electric Steel Structures Wood Coatings Pipes & Tubes
 
Automobiles & Ancillery
 
‘PIONEER COATS’ is a leading Paint manufacturer, who can supply quality paints to leading Bus Body builders in India. We can supply primers and paints for the application on chassis , inner bus body coatings , primers for the steel structures as well as P.U. , Stoving and Synthetic Enamel Top Coats.
 
  Product List for Commercial Vehicle Sectors
Two Pack Polyurethane Finishes (Auto)
Acrylic Auto Finish
N. C. Paints & Primers
Etch Primer (Yellow)
Epoxy H.B. Z/P Primer
Q.D. Enamel Paints & Primers
Automobiles & Ancillery Automobiles & Ancillery A) Commercial vehicle Sectors
     
A) Commercial vehicle Sectors A) Commercial vehicle Sectors A) Commercial vehicle Sectors
 
 

 
Technical Information for the above Products :
Two Pack Polyurethane Finishes (Auto)
 

Two pack Acrylic polyol based system cured with polyisocynate adduct. Specially designed to meet the requirements of Automobiles industry, Electric industries, electronic, mechanical & other industries

Main Properties :
1) Sp. Gravity : Solid 1.20 (± 0.05kg) per Ltr.
2) Non-Volatile Content : 60% (± 5%)
3) Supply Viscosity : 80 (± 10 sec) at Room Temp
4) Application viscosity : 20-22 Sec
5) Covering : 100 ± 10Sq.fts

Dry film Properties :
1) Gloss : 90 units at angle 60°c
2) Dry film thickness : 25 to 30 microns
3) Scratch hardness : Passes 2000gms
2) Flexibility test : 1/8” Passes
3) Impact test : 60cm (500gms) passes
4) Adhesion ( Cross Cut) : 100% (TG-5) for 1mm
5) Mar Resistance : after 7 days, no scratch marks, when nail run over it
6) Film appearance : Smooth & Glossy

 

Acrylic Auto Finish : NC ACRYLIC AUTOMOTIVE TOP COAT :


This Paint is based on combination of NC & Thermoplastic Acrylic resin. It has excellent outdoor durability as well as adhesion scratch hardness and toughness along with quick drying properties. The only disadvantage of the paint is moderate gloss and poor petrol & diesel resistance.

Physical Properties.
1. Viscosity : 120 seconds by Ford Cup No. 4
2. Wet /Litre : 1.15 ± 0.05 kg/ltr.
3. Mixing Ratio : Paint - 1 Part
Thinner – 1 Part
4. Spraying Viscosity : 20-22 Seconds by Ford Cup No.4

Dry Film Properties :
1. Adhesion : By Cross Cut test - Passes
2. Drying Time : S.D. - 5-10 minutes / Tack Free – 3-4 Hrs. / Hard Dry – 18 Hrs.
3. Finish : Smooth & Semi Glossy.
4. Covering Power (wet Opacity ) : 100 ± 10 sq. ft. / Litre
5. Flexibility : Passes on 1/8” mandrel
6. Scratch Hardner : Passes 2 Kg.
7. Salt Spray Resistance : Passes for 144 Hrs.
(5% NACL Solution)
8. Dry Film thickness 20 ± 5 microns
9 . Impact Test : Passes for 20cm Height 1Kg. Load
10.. Gloss : 75 ± 5 units on 60° angle glossmeter

1K POLYURETHANE METALLIC FINISH:

One pack Acrylic polyurethane-based system specially designed to meet the requirements of Automobile Industry & Bus Bodies. Also can be used for Electric Industry, Electronic, Mechanical & other industry. This Polyurethane Metallic Finish is a Single Pack base coat. To achieve high gloss metallic finish, apply 2K Polyurethane finish clear lacquer on this base coat. This coating has excellent durability & colour retention.

Physical Properties.

1. Composition : Acylic Base
2. Sp. Gravity : 1 (± 0.05) Kg. per Ltr.
3. Non-Volatile Content : 30 (± 5) %
4. Supply Viscosity : 60 (± 20 sec) at R.T.
5. Application viscosity : 18 - 22 Sec
6. Covering Capacity : 150 ± 10Sq.fts Per coat.
7. Drying Time : Surface Dry 5 min.
Tack Free 30 min.
Hard Dry 2 hrs.
10. Recoatability : After 1 hrs.
11. Intercoat Adhesion : Excellent.

DRY FILM PROPERTIES :
1. Gloss : Metallic finish
2. Dry film thickness : 10 to 15 microns
3. Adhesion ( Cross Cut) : Passes 100% (TG-5) for 1mm
4. Film appearance : Smooth & Metallic matt. Finish

 


N.C. Paints & Primers :NC PRIMER SURFACER GREY

This primer / surfacer is formulated to get excellent adhesion to metal, as well as inter coat adhesion to etch primer & NC Acrylic Top coat Paint. It also has excellent sanding property along with flexibility. The incorporation of anticorrosive pigments in primer gives good corrosion resistance.

Physical Properties :

Viscosity : 100 ± 20 seconds by Ford Cup No. 4
Wet / Litre : 1.2 ± 0.05 Kg. / Litre
Spraying Viscosity : 20 – 22 Seconds by Ford Cup No.4

Dry Film Properties :

Adhesion : By Cross Cut test - Passes
Drying Time : S.D. - 5-10 minutes
Tack Free – 1-2 Hrs.
Hard Dry – 10 Hrs.
Recoating Period : 5 – 6 Hrs.
Finish : Smooth & Matt.
Covering Power (wet Capacity ) : 100 ± 10 sq. ft.
Scratch Hardner : Passes 2Kg. Load.
Salt Spray Resistance Passes for 150 Hrs.(For total system)
(5% NACL Solution)
Dry Film thickness 25 ± 5 microns
Impact Test : Passes for 20cm Height 1Kg. Load

NC ACRYLIC AUTOMOTIVE TOP COAT :

This Paint is based on combination of NC & Thermoplastic Acrylic resin. It has excellent outdoor durability as well as adhesion scratch hardness and toughness along with quick drying properties. The only disadvantage of the paint is moderate gloss and poor petrol & diesel resistance.

Physical Properties.

1. Viscosity : 120 seconds by Ford Cup No. 4
2. Wet /Litre : 1.15 ± 0.05 kg/ltr.
3. Spraying Viscosity : 20-22 Seconds by Ford Cup No.4
4. Shelf Life : 1 year.

Dry Film Properties :

Adhesion : By Cross Cut test - Passes
Drying Time : S.D. - 5-10 minutes
Tack Free – 3-4 Hrs.
Hard Dry – 18 Hrs.
Recoating Period : 2 – 3 Hrs.
Finish : Smooth & Semi Glossy.
Covering Power on (wet Opacity ) : 100 ± 10 sq. ft. / Litre
6. Scratch Hardner : Passes 2 Kg.
8. Salt Spray Resistance Passes for 144 Hrs. (5% NACL Solution)
9. Dry Film thickness 20 ± 5 microns
10. Impact Test : Passes for 20cm Height 1Kg. Load
11. Gloss : 75 ± 5 units on 60° angle glossmeter

 

TWO PACK ETCH ( WASH ) PRIMER YELLOW.

Etch Primer is a anti-corrosive primer, having excellent adhesion on Galvanized sheet, Aluminum & Mild Steel . It is based on polyvinyl Butryl resin, and anti-corrosive pigment. This primer is specially formulated as fast drying primer with longer pot life. This primer is suitable for over coating by all types of paint systems like Q.D., Epoxy, PU NC etc

SYSTEM : Polyvinyl Butryl resin & Phosphoric acid as catalyst.
SUPPLY VISCOSITY : 70( ± )10 seconds by Ford Cup B-4
Mixing Ratio : 1 Part Etch Primer & 1 Part Etch Primer Hardner
Spraying Viscosity : 18 to 22 seconds by Ford cup B-4
Shelf Life : Maximum 6 months
Film thickness : Dry film thickness 5 to 10 microns.
Pot life : 4 - 6 hours.

Dry Film Properties :

Adhesion : Excellent (Passes crosscut test)
Finish : Smooth & Matt
Drying Time : Surface Dry :- 3 – 5 Minutes
Tack free : 10 – 20 Minutes
Hard Dry : 2 – 3 Hours
Colour : pale yellow / pale brown
Spreading capacity : 150( ± )10sq.ft. per one coat per liter.
Salt spray resistance : Passes for 96 hours for 50 microns DFT 5 % Nacl solution
Recoatability : Primer /surfacer should be applied after 2-3 hrs. but not after 16 hrs.


 
 

High Build Epoxy Zinc Phosphate GREY PRIMER

This is high performance high build primer having excellent adhesion, corrosion resistance properties. It also has excellent covering capacity & flexibility.

Physical Properties :
Viscosity : Thyrotrophic in nature
Wet / Liter : 1.60 ± 0.05 Kg. / Ltr. (Base)
0.94 ± 0.02 Kg. / Ltr. (Hardner)
3. Covering Capacity : 130 ± 10 Sq. ft. per litr. Per one coat
4. Non-volatile content : 70 ± 2 % by weight
5. Application Viscosity : 25 Sec. by B 4 Cup at Room Temp.

Dry Film Properties:

1. Adhesion : By Cross Cut test - Passes (on M. S. Panel)
2. Drying Time : S.D. - 20-30 minutes
Tack Free – 3-4 Hrs.
Hard Dry – 10 - 18Hrs.
3. Finish : Smooth & Egg Shell.
4. Scratch Hardner : Passes 2Kg. Load.
5. Salt Spray Resistance : Passes for 300 Hrs. At dft 50 to 60 microns
(5% NACL Solution)
6. Pot Life : minimum 6 hours.
7. Dry Film thickness : 35 – 40 microns per one coat.

Two Pack EPOXY ZINC PHOSPHATE GREY PRIMER (DA-100)

This is a high performance Epoxy primer cured with polyamide resin. The specialty of this primer is that it has direct adhesion to Aluminum & galvanize surface. This primer can be forced dry at 70 to 80 C for 30 to 40 min. It has excellent adhesion, corrosion resistance as well as flexibility, recoat ability with Epoxy, PU & enamel paints

Physical Properties :

Viscosity : 60 (+/-) 10 second by Ford cup No. 4
Wet / Litre : 1.40 ± 0.05 Kg. / Litre
Spraying Viscosity : 22 – 25 Second by B – 4 Ford Cup.

Dry Film Properties :

1. Adhesion : Excellent after 24 hrs.
2. Drying Time : S.D. - 15 – 20 minutes
Tack Free – 3 – 4 Hrs.
Hard Dry – 16 – 20 Hrs.
3. Finish : Smooth & egg shell.
4. Scratch Hardner : 2 Kg. Load passes after 48 hrs.
5. Salt Spray Resistance : Passes for 225 Hrs.
(5% Nacl Solution)
6. Covering Capacity : 100 (+/-) 10 Sq. ft. per ltr. Per coat
7. Dry Film thickness : 20 - 25 microns per one coat.

Q.D. Paint & Primer
Syn. Q. D. Zinc Phosphate Grey Primer :

This is a fast drying primer having excellent adhesion, hardness as well as good corrosion resistance. It is suitable for fast production output, we can handle the job within 20-30 minutes after application at room temp. There is no need to cure at oven.

Physical Properties :

1.Viscosity : 60 (+/-) 10 second by Ford cup No. 4
2.Wet / Litre : 1.20 ± 0.05 Kg. / Litre
3. Degree of Dispersion : 5 + by H. G.
4. Spraying Viscosity : 22 – 25 Second

Dry Film Properties :

1. Adhesion : Excellent after 24 hrs.
2. Drying Time : Surface Dry - 5 – 7 minutes
Tack Free – 30 – 40 min.
Hard Dry – 12 – 16 Hrs.
3. Recoating Time - 4 to 6 Hrs
3. Finish : Smooth & matt.
4. Flexibility : Passes 1/4” on mandrel
5. Scratch Hardener : Passes 1200gms Load.(after48hrs.)
6. Salt Spray Resistance : Passes for 96 Hrs.
7. Covering Capacity : 110 (+/-) 10Sq. ft. per ltr. Per coat
8. Dry Film thickness : 25 – 30 microns per one coat.

 

Manufacturers And Suppliers - Industrial Paints, Automobiles Paints, Primers, Thinners, Epoxy Paint, Polyurethane Paints, Chlorinated Rubber Paints, Wood Sealer, Wood Melamine